CdS Thin Films Deposited by CBD Method on Glass
CdS thin film Chemical-bath-deposited method CIGS solar cell Direct energy band gap
font style='font-size:12px;'>
2012/4/5
CdS thin films were prepared by chemical-bath-deposited method and the effect of tempera-ture and time on the properties of CdS thin films was studied. Independent of the deposited temperature, the gr...
Photoluminescence enhancement in Yb3+:Er3+ co-doped eutectic Al2O3: SiO2 thin films by 980nm excitation
font style='font-size:12px;'>
2011/12/7
Si nanocrystals (nc-Si) are addressed in the eutectic Al2O3:SiO2 thin films co-doped with Er3+ and Yb3+ by the laser-induced crystallization (LIC). The thin films are originally synthesized on a silic...
层层静电自组装构筑壳聚糖/磷钨酸复合膜的研究（Construction of Composite Thin Films via Layer-by-layer Electrostatic Self-assembly of Chitosan/Phosphotungstate Acid）
壳聚糖/磷钨酸复合膜 层层自组装 多层膜
font style='font-size:12px;'>
2010/8/24
将正电荷的壳聚糖与负电荷的磷钨酸溶液通过静电作用交替沉积在基底上组装复合多层膜。使用紫外可见光谱(UV-Vis)、红外光谱(FTIR)、X-射线光电子能谱(XPS)、原子力显微镜(AFM)和循环伏安法(CV)等手段对复合膜进行了表征。UV-Vis结果显示多层膜在特征吸收峰处的吸光度数值随膜双层数增加逐渐增大，呈良好的线性关系，表明多层膜是均匀组装的；XPS和FTIR结果证实了壳聚糖和磷钨酸被组装到...
BST/Si-NPA复合薄膜的湿敏电容特性研究（Capacitive Humidity Sensing Properties of BST/Si-NPA Composite Thin Films）
钛酸锶钡 硅纳米孔柱阵列 复合薄膜 湿敏电容特性
font style='font-size:12px;'>
2010/8/25
本文采用溶胶-凝胶法和旋涂工艺，以Si-NPA为衬底，制备了钛酸锶钡(BST)/Si-NPA复合薄膜，并对其形貌、结构及湿敏电容特性进行了研究。结果表明，环境的相对湿度(RH)、测试信号频率和退火温度均对湿敏电容特性具有较大影响。在100 Hz的测试信号频率下，当环境的相对湿度从11%上升到95%时，BST/Si-NPA湿敏元件的电容增量可达起始值的4 400%，显示出较高的湿度敏感性。同时，元件...
Synthesis of pyrite thin films obtained by thermal sulfurating iron films at different sulfur atmosphere pressure
font style='font-size:12px;'>
2007/7/28
期刊信息
篇名
Synthesis of pyrite thin films obtained by thermal sulfurating iron films at different sulfur atmosphere pressure
语种
英文
撰写或编译
撰写
作者
Meng L,Liu Y H,Huang W
第一作者单位
浙江大学
刊物名称
Mater. Sci. Eng
页面
2...
溶胶浸渍模板法制备有序多孔氧化钛、氧化锌薄膜（Preparation of Ordered Porous TiO2 and ZnO Thin Films by Sol-dipping Template Method）
有序多孔薄膜 模板 氧化钛 氧化锌
font style='font-size:12px;'>
2010/8/18
采用溶胶浸渍模板法制备了有序多孔的氧化钛(TiO2)和氧化锌(ZnO)薄膜。首先，在洁净的玻璃基片上通过浸渍-提拉工艺组装有序的聚苯乙烯微球(PS)阵列模板；然后再采用溶胶浸渍法将TiO2和ZnO溶胶灌充到PS模板微球的间隙内；最后通过煅烧去除PS而得多孔薄膜。采用SEM观察了薄膜的表面形貌，并用XRD对薄膜的性能进行了表征。结果表明，溶胶的浓度对薄膜形貌有着显著的影响。经煅烧后，TiO2和ZnO...